» Titanium 15V 3Cr 3Al 3Sn

AMS 4914 - UNS R58153 - USWC 4914 (C)
Alloy 15-3-3-3 Ti is a solid welding wire produced conventionally and then surface cleaned to remove standard drawing lubricants.
This metastable beta Ti alloy is a high strength, heat-treatable material used in aerospace applications.

Ti 15-3-3-3 Foil available min. 0.03mm x 150mm width x coil
mostly in stock 0.6 mm often used in eye fgrames and other high flexible applications.

This HIGHSTRENGTH, COLDFORMABLE ALLOY is sometimes available as a wire with max. 12 mm diameter. Ti-15V-3Cr-3Sn-3Al is a metastable beta titanium alloy that offers substantial weight reductions over other engineering materials. In the solution treated condition, it has excellent cold formability; in aged condition, it has high strength. 15-3 is a production alloy that is currently used for critical applications on air and space vehicles. 15-3 is usually acceptable for use at temperatures up to 550°F (288°C). Strip is available in gauges from 0.016 in (0.4mm) to 0.094 in (2.4mm). At thinner gauges, 15-3 is less expensive than Ti Grade 5.

Composition Titanium 6Al4V Physical Data Titanium Alloys Mechanical Chemical Physical Properties Mechanical Data Titanium Grades 1 2 3 4 5 7 9 11 12 19 Beta C Fabrication Information

» Composition

C < 0.05 %
Fe < 0.25 %
N2 < 0.05 %
O2 < 0.13 %
H2 < 0.015 %
V 14-16 %
Cr 2.5-3.5 %
Zn 2.5 - 3.5 %
Al 2.5 - 3.5 %
Ti = Rem

» Physical Data

  Minimum Typical
Density g/cm3 (lb/cu.in)   4.78(0.173)
Beta Transus °C+/-15°C(°F)   750-770

» Mechanical Data

  Minimum Typical
Tensile Strength MPa(ksi) 1004 (144) 1045 (146)
0.2% Proof Stress MPa(ksi) 895 (130) 955 (139)
Elongation over 2 Inches % 19 18
Reduction in Area % 42 40
Elastic Modulus GPa(Msi)   82-111

» HEAT TREATMENT

Solution Temperature 1450°F(790°C) air cool equivalent
Solution Time 3-20 min
Aged Temperature 900°F(480°C) - 1150°F(620°C)
Aged Time 4-16 hrs